S-13MN.B

Наплавка S-13MN.B

Type Basic
Industry Heavy Equipment|Offshore structures|Energy & Power Plants|Steel Fabric
JIS Z3251 DFMA-250-B
EN
KS
AWS
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.


    ② Preheat at 200~300℃(392~572℉).


    ③ Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose because arc striking on the base metal is in danger of initiating cracking.


    ④ Pay attention not to exceed proper heat-input because excessive heat-input causes deterioration of impact values of all weld metal.
  • Purpose ① Low alloy high tensile steels
  • Attribute ① Iron powder and low hydrogen type electrode (high efficiency)


    ② Good crack resistance


    ③ Good X-ray performance


    ④ Good impact value at -50°C

S-711

Наплавка S-711

Type Basic
Industry
JIS Z3251 DFCrA-600-BR
EN
KS
AWS
  • Caution .
  • Purpose ① Mills to crush clinker in cement industry


    ② Screws in oil industry
  • Attribute ① Good wear resistance


    ② Austenite structure containing Cr-Carbide


    ③ Machining impossible (As welded)


    ④ Preheat at more than 150°C(302°F)

S-700B.B

Наплавка S-700B.B

Type Basic
Industry
JIS Z3251 DF3C-600-B
EN
KS
AWS
  • Caution ① Preheat at 150℃(302℉) or more than that in general.


    ② Postheat at about 600℃(1112℉), if possible.


    ③ In case of multi-layer build-up welding or welding base metal of hardening property, underlay with low hydrogen type carbon steel electrodes.


    ④ Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Preheat at more than 150°C(302°F)


    ② Postheat at about 600°C(1112°F), if possible


    ③ Martensite structure (All-weld metal)


    ④ Machining impossible (As welded)


    ⑤ Mostly suitable for soil abrasion

S-600B.B

Наплавка S-600B.B

Type Basic
Industry
JIS Z3251 DF2B-600-B
EN
KS
AWS
  • Caution ① Preheat at 150℃(302℉) or more than that in general.


    ② In case of multi-layer build-up welding or welding base metal of hardening property, underlay


    with low hydrogen type carbon steel electrodes.


    ③ Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Under-lay with low hydrogen type carbon steel electrode


    ② Preheat at more than 150°C(302°F)


    ③ Suitable for soil abrasion


    ④ Martensite structure (All-weld metal)

S-500B.B

Наплавка S-500B.B

Type Basic
Industry
JIS Z3251 DF2B-500-B
EN
KS
AWS
  • Caution ① Preheat at 150℃(302℉) and more than that in general.


    ② In case of multi-layer build-up welding or welding base metal of hardening property, underlay


    with low hydrogen type carbon steel electrodes.


    ③ Pay attention to blow hole at the arc starting.


    ④ Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Under-lay with low hydrogen type carbon steel electrode


    ② Preheat at more than 150°C(302°F)


    ③ Machining difficult

S-450B.B

Наплавка S-450B.B

Type Basic
Industry
JIS Z3251 DF2A-450-B
EN
KS
AWS
  • Caution ① Preheat at 150℃(302℉) and more than that in general.


    ② In case of multi-layer build-up welding, under-lay with low hydrogen type carbon steel electrodes.


    ③ Pay attention to blow hole at the arc starting.


    ④ Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Mixed metal structure of austenite and martensite


    ② Under-lay with low hydrogen type carbon steel electrode ③ Preheat at more than 150°C(302°F)

S-350B.B

Наплавка S-350B.B

Type Basic
Industry
JIS Z3251 DF2A-400-B
EN
KS
AWS
  • Caution ① Preheating is unnecessary, in general, large weldments of hardening property should be preheated.


    ② In case of high cooling speed, preheat or postheat to prevent difficulty of machining caused by hardening.


    ③ Pay attention to blow hole at the arc starting.


    ④ Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Medium abrasive resistance, impact resistance


    ② Machining possible


    ③ Low spatter


    ④ Good bead appearance


    ⑤ Hardness increased by quenching after machining

S-260A.B

Наплавка S-260A.B

Type Basic
Industry
JIS Z3251 DF2A-300-B
EN
KS
AWS
  • Caution ① Preheating is unnecessary, in general, in case of multi-layer welding of low alloy steel and high carbon steel, preheat at about 150℃(302℉).


    ② Adopt back step method or strike arc on a small steel plate prepared for this particular purpose for preventing blow hole at the arc starting.


    ③ Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Light abrasive resistance, impact resistance


    ② Good cutting properties


    ③ Easy to remove slag


    ④ Low spatter


    ⑤ Good bead appearance

S-350A.R

Наплавка S-350A.R

Type Rutile
Industry
JIS Z3251 DF2A-350-R
EN
KS
AWS
  • Caution ① In case of hardfacing on large size cast steel, low alloy steel and high carbon steel, preheat at 150℃(302℉) and more than that.


    ② The groove repairing is prone to slag inclusion. Adjust the holding angle of the electrodes.


    ③ Dry the electrodes at 70~100℃(158~212℉) for 60 minutes before use
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Medium abrasive resistance, impact resistance


    ② Machining / Quenching possible


    ③ Easy to remove slag


    ④ Good bead appearance

S-240A.R

Наплавка S-240A.R

Type Rutile
Industry
JIS Z3251 DF2A-250-R
EN
KS
AWS
  • Caution ① Hardfacing large size cast steel and forging, low alloy steel and high carbon steel requires preheating at 150℃(302℉) and more than that.


    ② The groove repairing is prone to slag inclusion. Adjust the holding angle of the electrodes.


    ③ Dry the electrodes at 70~100℃(158~212℉) for 60 minutes before use.
  • Purpose ① Hardfacing of rollers, gears, crane wheels and abrasive parts
  • Attribute ① Light abrasive resistance, impact resistance


    ② Good cutting properties


    ③ Stable arc


    ④ Easy to remove slag


    ⑤ Low spatter


    ⑥ Good bead appearance