サブマージアーク溶接材料

Superflux55ULT x H-14

Superflux 55ULT Superflux55ULT x H-14

Type
Industry
JIS Z3352 S A FB 1 / Z3351 YS-S6
EN ISO 14174 S A FB 1 / 14171 S4
KS KS B0531 S502-H
AWS A5.17/ASME SFA5.17 F7A(P)8-EH14
  • Caution ① Dry the flux at 300~350°C (572~662°F ) for 60 minutes before use.

    ② Suitable welding condition for 1st pass in the groove is 500~550A, 26~30V and 30~40Cpm to prevent hot cracking and obtain good slag removal.

    ③ Preheat at 50~100°C depending on kind of base metal and plate thickness.

    ④ When restraint stress is high or welding a thick plate, preheat according to rules.
  • Purpose ① Offshore

    ② Shipbuilding

    ③ Cryogenic applications
  • Attribute ① Good impact value and CTOD at low temperature

    ② Low hydrogen content

    ③ Tandem, multi-electrode applicable

    ④ Density : 1.2g/cm3
top