Комбинация флюса и проволоки

Superflux800T x A-2

Superflux 800T Superflux800T x A-2

Type
Industry
JIS Z3352 S A AB 1 / Z3351 YS-M3
EN ISO 14174 S A AB 1 / 14171 S2Mo
KS
AWS A5.23/ASME SFA5.23 F8A4-EA2-A2
  • Caution ① Dry at 300~350°C (572~662°F ) for 60 minutes before use.


    ② In case of multi-layer welding of the thick plate, to prevent cracks, low current and low speed welding should be performed on the lower layer.


    ③ If weld heat input is managed below 31KJ/cm, a better impact toughness can be achieved.


    ④ When restraint stress is high or welding a thick plate, preheat according to rules.
  • Purpose ① Windtower


    ② Power plant
  • Attribute ① Good bead appearance


    ② Easy to remove slag


    ③ Low consumption of flux


    ④ Density : 1.1g/cm3

Superflux800T x M-12K

Superflux 800T Superflux800T x M-12K

Type
Industry
JIS Z3352 S A AB 1 / Z3351 YS-S2Si
EN ISO 14174 S A AB 1 / 14171 S2Si
KS
AWS A5.17/ASME SFA5.17 F7A8-EM12K
  • Caution ① Dry at 300~350°C (572~662°F ) for 60 minutes before use.

    ② In case of multi-layer welding of the thick plate, to prevent cracks, low current and low speed welding should be performed on the lower layer.

    ③ If weld heat input is managed below 31KJ/cm, a better impact toughness can be achieved.

    ④ When restraint stress is high or welding a thick plate, preheat according to rules."
  • Purpose ① Windtower

    ② Power plant
  • Attribute ① Good bead appearance

    ② Easy to remove slag

    ③ Low consumption of flux

    ④ Density : 1.1g/cm3