Комбинация флюса и проволоки

S-900SP x A-2

S-900SP S-900SP x A-2

Type
Industry
JIS Z3352 S A AB 1 / Z3351 YS-M3
EN ISO 14174 S A AB 1 / 14171 S2Mo
KS
AWS A5.23/ASME SFA5.23 F9A2-EA2(P2)-G
  • Caution ① Dry at 300~350°C (572~662°F ) for 60 minutes before use.

    ② If weld heat input is managed below 31KJ/cm, a better impact toughness can be achieved.

    ③ When restraint stress is high or welding a thick plate, preheat according to rules.
  • Purpose ① Pipe line
  • Attribute ① Good resistance to porosity on rust, scales and primers • High speed welding (Longtudinal pipes)

    ② Density : 1.2g/cm3

S-900SP x M-12K

S-900SP S-900SP x M-12K

Type
Industry
JIS Z3352 S A AB 1 / Z3351 YS-S3
EN ISO 14174 S A AB 1 / 14171 S2Mo
KS
AWS A5.17/ASME SFA5.17 F7A4-EM12K
  • Caution ① Dry at 300~350°C (572~662°F ) for 60 minutes before use.

    ② If weld heat input is managed below 30KJ/cm, a better impact toughness can be achieved.

    ③ When restraint stress is high or welding a thick plate, preheat according to rules.
  • Purpose ① Pipe line
  • Attribute ① Good resistance to porosity on rust, scales and primers • High speed welding (Longtudinal pipes)

    ② Density : 1.2g/cm3