HYUNDAI WELDING

Business Introduction

ALL PRODUCT

Stick Electrodes

S-9018.B3R

Heat-Resistant, Low-Alloy Steel S-9018.B3R

Type Basic
Industry
JIS E5518-1CM
EN E CrMo2 B 3 2
KS
AWS E8018-B2
  • Caution .
  • Purpose ① Low alloy steel (2.25%Cr-1%Mo)
  • Attribute ① Relevant elements P, Sn, As and Sb controlled (X-Factor ≤15ppm)
    ② Low-Hydrogen electrode (HDM ≤5ml/100g)
    ③ Iron powder type electrode (high efficiency)
    ④ Good impact value at low temperature

S-9016.B3R

Heat-Resistant, Low-Alloy Steel S-9016.B3R

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E6216-2C1M
EN ISO 3580-A - E CrMo2 B 1 2 H5
KS
AWS A5.5/ASME SFA5.5 E9016-B3
  • Caution .
  • Purpose ① Pressure vessels
    ② Powder plant
    ③ Low alloy steel (2.25%Cr-1.0%Mo)
  • Attribute ① Fire-coal Energy plant, Oil refinery, High temperature/ chemical facility
    ② 2.25% Cr-1.0% Mo Steel welding
    ③ Relevant elements P, Sn, As and Sb controlled (X-Factor ≤15ppm)
    ④ Low-Hydrogen electrode (HDM ≤5ml/100g)
    ⑤ Good impact value at low temperature

S-8018.B2R

Heat-Resistant, Low-Alloy Steel S-8018.B2R

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E5518-1CM
EN ISO 3580-A - E CrMo1 B 3 2 H5
KS
AWS A5.5/ASME SFA5.5 E8018-B2
  • Caution .
  • Purpose ① Low alloy steel (1.25%Cr-0.5%Mo)
  • Attribute ① Relevant elements P, Sn, As and Sb controlled (X-Factor ≤15ppm)
    ② Low-Hydrogen electrode (HDM ≤5ml/100g)
    ③ Iron powder type electrode (high efficiency) • Good impact value at low temperature

S-8015.B6

Heat-Resistant, Low-Alloy Steel S-8015.B6

Type Low-hydrogen Type
Industry Energy & Power Plants|Steel Fabrication
JIS
EN ISO 3580-A - E CrMo5 B 1 2
KS
AWS A5.5/ASME SFA5.5 E8015-B6
TTR
  • Caution .
  • Purpose .
  • Attribute .

S-8016.B6

Heat-Resistant, Low-Alloy Steel S-8016.B6

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS
EN ISO 3580-A - E CrMo5 B 1 2
KS
AWS A5.5/ASME SFA5.5 E8016-B6
  • Caution .
  • Purpose ① Low alloy steel (5%Cr-0.5%Mo)
  • Attribute ① Low hydrogen type electrode
    ② Good creep resistance at high temperature
    ③ Good crack resistance

S-8016.B2R

Heat-Resistant, Low-Alloy Steel S-8016.B2R

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E5516-1CM
EN ISO 3580-A - E CrMo1 B 1 2 H5
KS
AWS A5.5/ASME SFA5.5 E8016-B2
  • Caution .
  • Purpose ① Pressure vessels
    ② Powder plant
    ③ Low alloy steel (1.25%Cr-0.5%Mo
  • Attribute ① Fire-coal Energy plant, Oil refinery, High temperature/ chemical facility
    ② 2.25% Cr-1.0% Mo Steel welding
    ③ Relevant elements P, Sn, As and Sb controlled (X-Factor ≤15ppm)
    ④ Low-Hydrogen electrode (HDM ≤5ml/100g)
    ⑤ Good impact value at low temperature

S-8015.B8

Heat-Resistant, Low-Alloy Steel S-8015.B8

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS
EN ISO 3580-A - ECrMo9 B 3 2 H5
KS
AWS A5.5/ASME SFA5.5 E8015-B8
  • Caution .
  • Purpose ① Pressure vessels
    ② Powder plant
    ③ Low alloy steel (9%Cr-1%Mo
  • Attribute ① 9% Cr Steel Welding for superheated pipe (boilers and refinery)
    ② Good resistance for high temperature creep
    ③ Anti-temperature / Anti-Corrosion

S-9016.B9

Heat-Resistant, Low-Alloy Steel S-9016.B9

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E6216-9C1MV
EN ISO 3580-A - E CrMo91 B 3 2 H5
KS
AWS A5.5/ASME SFA5.5 E9016-B91
  • Caution .
  • Purpose ① Heat resistant steel (9%Cr-1%Mo
  • Attribute ① Good creep resistance at high temperature
    ② Maximum service temperature at 650°C (1202°F)
    ③ Low-Hydrogen electrode (HDM ≤5ml/100g)

S-9015.B9

Heat-Resistant, Low-Alloy Steel S-9015.B9

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E6215-9C1MV
EN ISO 3580-A - E CrMo91 B 4 2 H5
KS
AWS A5.5/ASME SFA5.5 E9015-B91
  • Caution .
  • Purpose ① Heat resistant steel (9%Cr-1%Mo)
  • Attribute ① Good creep resistance at high temperature
    ② Maximum service temperature at 650°C (1202°F) • Low-Hydrogen electrode (HDM ≤5ml/100g)
    ③ Good performance with DCEP

S-8016.B5

Heat-Resistant, Low-Alloy Steel S-8016.B5

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS
EN ISO 3580-B - E5518-C1M
KS
AWS A5.5/ASME SFA5.5 E8016-B5
  • Caution .
  • Purpose ① Low alloy steel (0.5%Cr-1%Mo)
  • Attribute ① Good mechanical properties

S-9018.B3

Heat-Resistant, Low-Alloy Steel S-9018.B3

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E6218-2C1M
EN ISO 3580-A - E CrMo2 B 3 2
KS
AWS A5.5/ASME SFA5.5 E9018-B3
  • Caution ① Preheat at 200~350℃(392~662℉) and postheat at 680~730℃(1256~1346℉).
    ② Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
  • Purpose ① Low alloy steel (2.25%Cr-1%Mo)
  • Attribute ① Maximum service temperature at 600°C (1112°F)
    ② Good mechanical properties
    ③ Good creep resistance
    ④ Iron powder low hydrogen type electrode (high efficiency).

S-9016.B3

Heat-Resistant, Low-Alloy Steel S-9016.B3

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E6216-2C1M
EN ISO 3580-A - E CrMo2 B 1 2
KS
AWS A5.5/ASME SFA5.5 E9016-B3
  • Caution .
  • Purpose ① Low alloy steel (2.25%Cr-1%Mo)
    ② Pressure vessels
    ③ Power plant
  • Attribute ① Maximum service temperature at 600°C (1112°F)
    ② Good mechanical properties
    ③ Good creep resistantance

S-8018.B2

Heat-Resistant, Low-Alloy Steel S-8018.B2

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E5518-1CM
EN 1599 - E CrMo1 B 3 2
KS
AWS A5.5/ASME SFA5.5 E8018-B2
  • Caution ① Preheat at 150~300℃(302~572℉) and postheat at 670~730℃(1238~1346℉).
    ② Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
    ③ Keep the arc as short as possible.
  • Purpose ① Low alloy steel (1.25%Cr-0.5%Mo)
  • Attribute ① Iron powder and low hydrogen type electrode (high efficiency)
    ② Good mechanical properties
    ③ Good creep resistantance

S-8016.B2

Heat-Resistant, Low-Alloy Steel S-8016.B2

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E5516-1CM
EN ISO 3580-A - E CrMo1 B 1 2
KS
AWS A5.5/ASME SFA5.5 E8016-B2
  • Caution ① Preheat at 150~300℃(302~572℉) and postheat at 670~730℃(1238~1346℉).
    ② Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
    ③ Keep the arc as short as possible.
  • Purpose ① Low alloy steel (1.25%Cr-0.5%Mo)
    ② Pressure vessels
    ③ Power plant
  • Attribute ① Maximum service temperature at 550°C (1022°F)
    ② Good mechanical properties
    ③ Good creep resistance

S-8016.B1

Heat-Resistant, Low-Alloy Steel S-8016.B1

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS
EN ISO 3580-A - E CrMo0.5 B 1 2
KS
AWS A5.5/ASME SFA5.5 E8016-B1
  • Caution ① Preheat at 150~250℃(302~482℉) and postheat at 628~680℃(1162~1256℉).
    ② Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
    ③ Keep the arc as short as possible.
  • Purpose ① Low alloy steel (0.5%Cr-0.5%Mo)
    ② Pressure vessels
    ③ Power plant
  • Attribute ① Good crack resistance

S-7018.A1

Heat-Resistant, Low-Alloy Steel S-7018.A1

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E4918-1M3
EN ISO 3580-A - E Mo B 3 2
KS
AWS A5.5/ASME SFA5.5 E7018-A1
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
    ② Preheat at 100~200℃(212~392℉) and postheat at 620~680℃(1148~1256℉).
    ③ Keep the arc as short as possible.
  • Purpose ① Low alloy steel (0.5% Mo)
    ② Pressure vessels
  • Attribute ① Good mechanical properties
    ② Good bead appearance
    ③ Iron powder type electrode (high efficiency)

S-7016.A1

Heat-Resistant, Low-Alloy Steel S-7016.A1

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3223 E4916-1M3
EN ISO 3580-A - E Mo B 1 2
KS
AWS A5.5/ASME SFA5.5 E7016-A1
  • Caution ① Preheat at 100~200℃(212~392℉) and postheat at 620~680℃(1148~1256℉).
    ② Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.
    ③ Keep the arc as short as possible.
  • Purpose ① Low alloy steel (0.5% Mo)
    ② Pressure vessels
  • Attribute ① Good mechanical properties
    ② Good bead appearance

S-7010.A1

Heat-Resistant, Low-Alloy Steel S-7010.A1

Type Cellulosic
Industry Energy & Power Plants|Steel Fabrication
JIS
EN ISO 2560-A - E42 0 Mo C 1 5
KS
AWS A5.5/ASME SFA5.5 E7010-A1
  • Caution ① Preheat at 100~200℃(212~392℉) and postheat at 620~680℃(1148~1256℉).
    ② Dry the electrodes at 70~100℃(158~212℉) for 30~60 minutes before use.
  • Purpose ① Low alloy steel (0.5% Mo)
    ② Pipe line
  • Attribute ① Good X-ray performance
    ② Good mechanical properties